Properties | 20/30 | 30/45 | 35/50 | 50/70 | 70/100 | 100/150 | 160/220 |
Penetration (0.1 mm) | 20-30 | 30-45 | 35-50 | 50-70 | 70-100 | 100-150 | 160-220 |
Ring & Ball | 55-63 | 52-60 | 50-58 | 46-54 | 43-51 | 39-47 | 30-38 |
Breaking point (oC) | - | -5 | -5 | -8 | -10 | -12 | -15 |
Viscosity (mm2/s) | 530 | 400 | 370 | 295 | 230 | 175 | 135 |
Flashpoint (oC) | 240 | 240 | 240 | 230 | 230 | 230 | 220 |
Properties | 75/30 | 85/25 | 85/40 | 95/30 | 100/25 | 115/15 | 125/30 |
Penetration (0.1 mm) | 25-35 | 20-30 | 35-45 | 25-35 | 20-35 | 10-20 | 20-35 |
Ring & Ball | 70-80 | 80-90 | 80-90 | 90-100 | 100-110 | 100-110 | 120-130 |
Breaking point (oC) | -12 | -10 | -20 | -15 | -15 | -10 | -20 |
Flash point (oC) | 230 | 240 | 240 | 240 | 240 | 250 | 260 |
Property | Unit | Test Method | 250/330 | 160/200 | 100/150 | 70/100 | 50/70 | 40/60 | 35/50 | 30/45 | 20/30 |
Penetration at 25 oC | 0.1mm | EN 1426 | 250-330 | 160-220 | 100-150 | 70-100 | 50-70 | 40-60 | 35-50 | 30-45 | 20-30 |
Softening Point | oC | EN 1427 | 30-38 | 35-43 | 39-47 | 43-51 | 46-54 | 48-56 | 50-58 | 52-60 | 55-63 |
Change of Mass Maximum | % | - | 1 | 1 | 0.8 | 0.8 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 |
Retained Penetration Minimum | % | - | 35 | 37 | 43 | 46 | 50 | 50 | 53 | 53 | 55 |
Softening Point after Hardening Minimum | oC | EN 1427 | 32 | 37 | 41 | 45 | 48 | 49 | 52 | 54 | 57 |
Flash Point Minimum | oC | EN22592 | 220 | 220 | 230 | 230 | 230 | 230 | 240 | 240 | 240 |
Solubility Minimum | % (m/m) | EN 12592 | 99 | 99 | 99 | 99 | 99 | 99 | 99 | 99 | 99 |
Properties | Test Method | 75/30 | 85/25 | 85/40 | 95/25 | 105/35 | 115/15 |
Softening point oC | BS 2000: Part 58 | 75 ±5 | 85±5 | 85±5 | 95±5 | 105±5 | 115±5 |
Penetration at 25 oC, DMM | BS 2000: Part 49 | 30 ±5 | 25±5 | 40±5 | 25±5 | 35±5 | 15±5 |
Loss on heating for 5 h at 163 loss by mass %, max oC | BS 2000: Part 45 | 0.2 | 0.2 | 0.5 | 0.2 | 0.5 | 0.2 |
Solubility in trichloroethylene % by mass, min | BS 2000: Part 47 | 99.5 | 99.5 | 99.5 | 99.5 | 99.5 | 99.5 |